2Broken joint repair of broken parts 2.1 Full-adhesive coating repair method 1 Scope of application For cast iron and cast aluminum alloy shell parts with less stress during work, such as the body of textile equipment, gearbox box, cylinder Cracks, perforations, chipping and corrosion at the cover and the like can be directly repaired by the adhesive method. 2Broken joint repair of broken parts 2.1 Full-adhesive coating repair method 1 Scope of application For cast iron and cast aluminum alloy shell parts with less stress during work, such as the body of textile equipment, gearbox box, cylinder Cracks, perforations, chipping and corrosion at the cover and the like can be directly repaired by the adhesive method. Spray Grain Texture PU Sandwich Panels
Spray Grain Texture PU Sandwich Panels
Rich selection of textures and colors meet different decoration requirements, giving the city and the buildings a new look.
2 open V-groove repair process 1-crack; 2r crack-stop hole; V-groove; 4-adhesive.
The crack on the side wall of the diesel engine is taken as an example. The crack on the side of the diesel engine is as an example: the crack length is only 100 mm, and the crack is not long and vertical. Although the part is subjected to a certain load, the stress of the crack is not large. The repairing process is as follows: the crack holes are drilled at both ends of the crack to prevent the crack from further expanding, and the diameter of the crack hole is 3 mm to 5 mm; the V-shaped groove is cut along the crack by a narrow hole, and the length exceeds 5 mm to 10 mm at both ends of the crack, and the depth is regarded as The thickness of the part is determined; the JW-1 epoxy repair adhesive is used to fill the V-groove, and after being fully cured, the surface is trimmed with a trowel and an abrasive cloth.
2.2 Auxiliary reinforcement bonding repair method 1 Scope of application Auxiliary reinforcement bonding repair method is suitable for medium-sized mechanical equipment with a load of about 1.0 MPa. " target=_blank> mechanical equipment, such as various large and medium-sized power machinery, textile machinery cylinders, cylinders Cracks, cracks, etc. of the cover, bed, etc. If it is difficult to ensure the strength requirement by full-glued repair, it is necessary to use an auxiliary reinforcement bonding repair method that combines the cement and some strengthening measures. Commonly used strengthening measures are: Reinforced steel plates, metal horse nails, metal wave keys and planted wire mesh, etc. Among these strengthening measures, some are through the bonding area, and some are directly repaired by mechanical connection.
2.2.2 Repair process Initially clean damaged parts, and determine auxiliary reinforcement measures according to the work and stress conditions of the parts. If nail metal nails are used, in addition to the bonding effect of the cement, the mechanical effect of the metal horse nails is used to achieve the repairing effect. The material of the metal horse nail is generally 35~45 steel, the structural size of the round horse nail is seen; the metal horse nail carefully cleans the glue joint, removes oil and performs surface chemical treatment; 2.2.3 repair example due to accident, a certain ship empty Serious cracking occurred on the upper, lower and right side of the press body, which was the damage on the right side. According to the damage, the adhesive is repaired with metal horse nails and glass fiber cloth. The adhesive is made of SW-2 epoxy structural adhesive. After repairing by the above method, the body has been working normally.
1-crack; 2-metal clasp.
The wavy key glue-bonding repair method combines the adhesive with a wavy key made of a high-strength alloy material with a special shape to improve the repair strength.
1 Scope of application ~45mm, repair of cracks and fractures of parts with force below 3MPa. For example, the repair of the cylinder block of a power machine, the casing of a large electric motor, the lathe, and the frame of a press.
2 repair process design to create the shape and size of the wave bond wave button. Flange size d=(1.4~1.6)b flange spacing/=(2~2.2)b, flange thickness t=(1.0~1.2)b. The neck width b of the wave bond is based on the size of the repairing mechanism. Whether the installation possibility and the riveting are convenient or not, generally b=3mm~6mm. The number of flanges of the wave key is generally 5, 7, and 9. In use, the number of flanges should be arranged, so that the machine can be improved. The force of the piece. The material of the wave key is generally selected from low carbon chromium nickel stainless steel such as 0Ci.18Ni9, 1Ci.18Ni9Ti, etc., which has good plasticity and has a great improvement in tensile strength after riveting and strengthening; There are two main parameters in the processing of the waveform groove groove: the groove depth T and the matching gap with the wave key 5 - T = 2 / 3h, H is the wall thickness of the repair area of ​​the machine; b0.1mm, cleaning wave key And the burr, oil stain and oxide layer of the corrugated groove, then apply the prepared adhesive around the wave bond to the wave groove. Then use the small wind wheel to rive the ball, the first wave button is flattened and the same method is used. Continue to embed and rive the second piece... After each layer is riveted, the accumulated chips need to be removed. The last layer of wave key riveting should be slightly lower than the plane of the workpiece, and then the groove is filled with adhesive until the adhesive is fully cured. Repair the surface with a small pneumatic wheel.
2.3.3 Repair example Deep 10mm crack, due to the huge impact load when punching work, the general full glue or auxiliary reinforcement glue can not guarantee the strength requirement. The wave bond is used in the construction to repair and repair. It has been used for more than ten years.
1-crack; 2-strength block; - skin wave bond; 4-stop hole.
2.4 Strengthening the block glue buckle legal reinforcement of the block glue buckle The essence of the law is: machining a certain shape of the cavity in the direction perpendicular to the crack or the fracture section, embedding the high-strength alloy steel block of the corresponding depth and shape , so that the load can be distributed to a larger area and away from cracks and breaks to ensure the quality of repair.
2.4.1 Scope of application For parts with a heavy load wall thickness exceeding 30 mm during operation, such as the bed of a large press, the beam of a hydraulic press, and the main frame of a rolling mill. If the wavy key glue is used only to obtain a reliable repair quality, the reinforcement block glue buckle must be applied as shown.
2.4.2 Design of the reinforcement block The shape of the reinforcement block is designed according to the damaged parts and stress conditions of the machine. The reinforcement blocks of different shapes and sizes are generally used, which are generally rectangular or semi-circular. The material of the reinforcement block is generally selected from 40Cr high-strength alloy inlaid wave keys. Before the wave bond is set, the steel should be carefully cleaned; 1-crack; 2-short pin; 3-rectangular reinforcement block; 4-thick-walled machine.
The processing of the reinforcement block pressing reinforcement block is first drawn on the blank according to the shape of the designed reinforcement block, and then the blank is placed on the part to be repaired, pressed by the pressure plate, drilled at the four corners, and inserted into the positioning pin, and then pressed Draw all the embossed bolt holes. Remove the blank and mill the excess metal by the centerline of the stitching.
Short-stitched pins with short stitches are made of the same material as the wave keys, such as low-carbon nickel stainless steel such as 1Cr18Ni9 "target=_blank> stainless steel, because these materials are easy to rive. Short cylindrical pins can not be too long. It is 8mm in diameter and 5mm in length, otherwise it is not easy to rive, and the combination is not good.
2.5 Repair of the damaged parts after the damage of the parts 2.5.1 Repair of the broken shaft Drill the matching hole and the exhaust hole at one end of the broken shaft, and the other end of the vehicle with the shaft that fits the hole. The clearance between the journal and the hole is 0.1mm. ~0.2mm, select phosphoric acid-copper oxide inorganic adhesive, see if the length can not be shortened after the broken shaft is repaired, the matching hole and the vent hole can be drilled at both ends of the broken shaft, and another mandrel is used to glue them together. See (b) together; to ensure the length of the shaft, the two ends of the shaft can be small, and then a metal ring is used to bond them together with an adhesive. Finally, the whole shaft is smashed, and the repaired shaft is perfect. For the whole, see (c); if the outer circle of the broken shaft does not match other parts, and does not hinder the appearance and work, a jacket can be prepared at the broken shaft and bonded with an adhesive. This repair is the simplest but the appearance is uneven, see (d).
2.5.2 Broken drill repair is generally repaired with an external steel sleeve. The broken glass fiber and the adhesive are mixed and filled in the cutting groove, and the broken drill which is repaired by the glue is rarely found to have looseness in the bonding part during use, and even if the force is too large and broken, the film portion is not loosened. This fully demonstrates the reliability of the bonding technology (see).
1-glued cullet; 2-break; 3-sleeve.
Drill-repair repair uses a jacket to repair broken drills. Although the process is simple, it affects chip removal during cutting and cannot drill deep holes. Http://news.chinawj.com.cn Editor: (Hardware Business Network Information Center) http://news.chinawj.com.cn
The PU foam is the most advanced and eco-friendly insulation material in the world. With the help of the back aluminum foil, the thermal preservation effect achieves the best.
The unique structure prevents the heat loss in winter. Meanwhile it reduces the heat of the summer sunshine.
Aceta paintcoat and flurocarbon paint of weather resistance performance are applied on surface of wall panel. It is reserved with superior self-cleaning, weather resistance, corrosion resistance and acid& alkali resistance performance.
Light weight with 3.7Kgs/m2 makes the installation easy.
The installation process is clean and tidy without any noise and dust, construction waste.
Different selections of accessories meet different effects.
High quality and stable performance: Manufactured in CNC automation production line, the product pass rate can reach 99.9% with stable chemical structure and physical structure.
Metal Cladding Panels,Insulation Metal Cladding Panels,Spray Grain Texture Pu Sandwich Panels,Spray Grain Texture Pu Sandwich Panels
Jinan Zhengtang Insulation Decoration Material Co.Ltd , https://www.ztwallsiding.com